System and method for purifying and preparing high-purity vanadium pentoxide powder

ABSTRACT

The present invention provides a system and method for purifying and preparing vanadium pentoxide powder. Industrial grade vanadium pentoxide is converted to vanadium oxytrichloride by low temperature fluidizing chlorination, wherein chlorinating gas is preheated via heat exchange between fluidizing gas and chlorination flue gas, and an appropriate amount of air is added to enable a part of carbon powder to combust so as to achieve a balanced heat supply during the chlorination, thereby increasing the efficiency of chlorination and ensuring good selectivity in low temperature chlorination. The vanadium oxytrichloride is purified by rectification, and then subjected to fluidized gas phase ammonification, thereby obtaining ammonium metavanadate, and further obtaining a high-purity vanadium pentoxide powder product through fluidized calcination. The system and method have advantages of favorable adaptability to raw material, no discharge of contaminated wastewater, low energy consumption and chlorine consumption in production, stable product quality etc.

CROSS REFERENCE TO RELATED APPLICATIONS

This application is the national phase entry of International Application No. PCT/CN2016/072524, filed on Jan. 28, 2016, which is based upon and claims priority to Chinese Patent Application No. CN201510051577.X, filed on Jan. 30, 2015, the entire contents of which are incorporated herein by reference.

TECHNICAL FIELD

The present invention relates to the fields of chemical engineering and materials, and more particularly to a system and method for purifying and preparing high-purity vanadium pentoxide powder.

BACKGROUND OF THE INVENTION

Vanadium pentoxide is one of the important industrial vanadium products, and widely applied in the production of alloy additives such as ferrovanadium and vanadium nitride, and in the fields of catalysts, colorants, cemented carbide additives and the like. With the continuous development of new energy technologies, there is a growing demand on high-purity vanadium pentoxide (with a purity of above 3N5) in the battery industry, including an all-vanadium redox flow battery (VRB) with good large-scale energy storage performance, a vanadate-based lithium-ion battery used for electric automobiles and the like. However, in general, only vanadium pentoxide with a purity of 2N5 (i.e. the product according with the specification in HGT 3485-2003) can be prepared by the existing industrial technology, which is difficult to meet requirements on vanadium pentoxide for the battery industry. Therefore, how to prepare high-purity vanadium pentoxide with low cost and high efficiency is one of the urgent issues need to be solved in the field of new energy technologies.

At present, a vanadium-leaching solution or a vanadium solution obtained by dissolving a vanadium-rich material (such as ammonium polyorthovanadate, ammonium metavanadate, industrial grade vanadium pentoxide, etc.) is usually used as a raw material, and purified by the methods such as chemical precipitation purification and/or solvent extraction/ion resin exchange etc. to obtain a purified vanadium solution; and then subjected to ammonium salt precipitation to obtain the purified ammonium polyvanadate or ammonium metavanadate precipitate; then, the precipitate is subjected to decomposition by calcination to obtain the high-purity vanadium pentoxide powder, as described in Chinese Patent Applications CN1843938A, CN102730757A, CN103145187A, CN103515642A, CN103194603A, CN103787414A, CN102181635A and CN103663557A, European Patent EP0713257B1, etc. In these methods, the process parameter for impurity removal is closely related to the content of the impurity in the raw material, thus the adaptability to the raw material is poor. Moreover, the calcium salt and magnesium salt scavengers or extractants, the acid and alkali reagents and ammonium salts for vanadium precipitation used in the purification process are also liable to introduce impurities. In order to improve the quality of the product, it is usually required to use expensive reagents with high purity, thereby leading to the following problems: the cost is too high, large-scale production cannot be implemented and the purity of the product is difficult to stabilize at above 3N5.

For the problems that the scavengers or extractants are liable to introduce impurities and the cost of the reagents used is too high, the relevant agencies also propose the use of the repeated precipitation method to achieve purification and impurity removal of a vanadium solution; that is, by using the ammonium salt precipitation characteristic of the vanadium-containing solution, vanadium is selectively precipitated out, to confine a part of the impurity ions to the solution after precipitation; the resulting ammonium salt precipitate is dissolved and then multiple repeated operations are conducted, to obtain more pure ammonium polyorthovanadate or ammonium metavanadate precipitate; and the precipitate is subjected to decomposition by calcination to obtain a high-purity vanadium pentoxide powder, as described in Chinese Patent Applications CN103606694A, CN102923775A, etc. This process effectively reduces the amount of the reagents used and the possibility that the reagents introduce impurities. However, the dissolution-precipitation process still requires use of a large quantity of high-purity acid and alkali reagents and ammonium salts, therefore the cost of purification is still high; and the cumbersome multiple precipitation operations not only lower the production efficiency but also lead to a significant decline in the direct recovery rate of vanadium. In addition, in the above-mentioned solution purification methods, extraction/back extraction, precipitation, washing and other operation steps will produce a large amount of waste water mainly containing a small quantity of vanadium ions and ammonium ions and a large amount of sodium salts, which results in difficult treatment and outstanding problem of pollution and also seriously restricts the large-scale industrial application of the methods.

Due to the large difference in the boiling points and saturated vapor pressures of metal chlorides, different metal chlorides are easily separated by distillation/rectification. Raw material chlorination—purification by rectification—subsequent treatment is a commonly-used preparation process for high-purity materials such as high-purity silicon (polysilicon), high-purity silicon dioxide, and the like. Because of a very large difference between boiling points of the chloride of vanadium, vanadium oxytrichloride, and the chlorides of common impurities such as iron, calcium, magnesium, aluminum, sodium, potassium and the like, high-purity vanadium oxytrichloride is easily obtained by rectification, and high-purity vanadium pentoxide can be prepared by subjecting the high-purity vanadium oxytrichloride to hydrolysis and ammonium salt precipitation, supplemented by calcination. Therefore, the use of the chlorination method for the preparation of high-purity vanadium pentoxide has a greater advantage in principle. In fact, the use of the chlorination method for the preparation of high-purity vanadium pentoxide is not only feasible in principle, but also has been implemented in the laboratory by the researchers of Iowa State University in the United States as early as the 1960s (Journal of the Less-Common Metals, 1960, 2: 29-35). They employed ammonium polyorthovanadate as a raw material, and prepared the crude vanadium oxytrichloride by chlorination with addition of carbon, then obtained high-purity vanadium oxytrichloride through purification by distillation, and conducted ammonium salt precipitation to obtain high-purity ammonium metavanadate, and finally calcined high-purity ammonium metavanadate at 500-600° C., to obtain the high-purity vanadium pentoxide powder. However, a large amount of wastewater containing ammonia and nitrogen will be produced in the precipitation and the washing processes, leading to difficult treatment. Moreover, the study only realizes the intermittent preparation of high-purity vanadium pentoxide by the chlorination method with the laboratory equipment, and cannot provide related information on how to use the chlorination method for continuous preparation of high-purity vanadium pentoxide on an industrial scale. It may be for exactly these reasons that the report on continuous preparation of high-purity vanadium pentoxide by the chlorination method is difficult to find in the decades after the study.

Recently, Chinese Patent Application CN103130279A proposes a method for preparing high-purity vanadium pentoxide by using the chlorination method with a vanadium-iron magnetic iron ore, vanadium slag, vanadium-containing catalyst and other materials containing vanadium as raw materials. A mixture of chlorides of vanadium is obtained through chlorination with addition of carbon—dust removal—condensing, and vanadium tetrachloride is separated through rectification to obtain pure vanadium oxytrichloride, then the vanadium oxytrichloride is fed into an ultrapure aqueous solution or ultrapure aqueous solution of ammonia and precipitated, and the precipitate is filtered, dried and calcined to obtain vanadium pentoxide. This patent has the following deficiencies: (1) similar to the above study of Iowa State University in the United States, this patent actually provides the basic flow of chlorination only, lacking the specific operable solutions. For example, the method of chlorination comprises both boiling chlorination and molten salt chlorination, which are completely different methods of chlorination. For another example, concerning the chlorination reactor, it is proposed to use reactors such as “rotary kiln, fluidized furnace, boiling furnace, shaft furnace, multi-hearth furnace” and the like, which actually covers almost all of the commonly-used mainstream reactors in the metallurgical industry; however, different reactors' requirements for raw materials differ greatly. For example, the shaft furnace can only handle “coarse” particles with a particle size more than 8 mm, and needs to conduct pelleting and sintering pretreatment when “fine” particles are processed, while boiling chlorination is generally suitable for the treatment of fine particles. Therefore, a particular vanadium raw material cannot be directly applied to rotary kiln, fluidized furnace, boiling furnace, shaft furnace, multi-hearth furnace and other reactors. Moreover, the “fluidized furnace” and “boiling furnace” are essentially the same, just different in names; therefore, since these reactors vary widely in operation mode and condition, the method cannot actually be implemented on the condition that only basic flow is provided. (2) Vanadium oxytrichloride is fed into the ultrapure aqueous solution for hydrolysis. However, because vanadium pentoxide is easily dissolved in the hydrochloric acid solution, the recovery rate of precipitation of vanadium is too low. Moreover, in the hydrochloric acid solution with an HCl concentration more than 6.0 mol/L, when vanadium pentoxide is dissolved, it will be reduced to VOCl₂ and chlorine gas is released, which will further reduce the recovery rate of precipitation of vanadium. Precipitation and washing processes will inevitably produce a large amount of hydrochloric acid solution containing vanadium, and it is difficult to effectively achieve a comprehensive treatment.

In addition, for large-scale industrial applications, there still exists the following two problems in the existing technologies for chlorination of vanadium raw materials: (1) calcination for chlorination of vanadium raw materials is a strong exothermic process, and in addition to preheating the solid and gas reaction materials, the heat generated by the chlorination reaction still needs to be removed by furnace wall heat dissipation to stabilize the temperature in the chlorination; therefore, both the solid and gas are usually enters the reactor at a temperature of near room temperature, and only can participate in the reaction after been preheated by the heat produced from the chlorination reaction, resulting in too low efficiency of reaction in part of the chlorination reactor; (2) since the heat produced by the chlorination reaction needs to be removed through dissipation of a large amount of heat to maintain the operation temperature, the operating condition and environmental climate change are both liable to cause fluctuations in chlorination temperature, resulting in reduction of selectivity in chlorination and efficiency, and it is needed to use a reasonable method for balanced supply of heat and temperature regulation. Therefore, reasonable heat supply and temperature control must be provided. Only in this way, it is possible to effectively improve the efficiency of chlorination and obtain stable chlorination temperature, so as to ensure the selectivity in the chlorination to effectively inhibit the chlorination of impurities.

Therefore, achieving the regulation of chlorination process, improving the direct recovery rate of vanadium, avoiding the production of a large amount of ammonia-nitrogen wastewater and increasing the efficiency of purification of vanadium pentoxide by innovation of the process and technology, are the keys to increase the economy of the technology for purifying and preparing high-purity vanadium pentoxide through the chlorination method.

SUMMARY OF THE INVENTION

In view of the above problem, the present invention proposes a system and method for purifying and preparing high-purity vanadium pentoxide powder, to ensure good selectivity in low temperature chlorination, avoid the production of a large amount of wastewater containing ammonia and nitrogen, and reduce the energy consumption in the production of high-purity vanadium pentoxide and the operation cost. In order to achieve these objects, the present invention adopts the following technical solutions.

The present invention provides a system for purifying and preparing high-purity vanadium pentoxide powder, comprising feeding device 1, low temperature chlorination fluidized bed 2, rectification and purification device 3, gas phase ammonification fluidized bed 4, ammonium metavanadate feeding device 5, calcination fluidized bed 6, tail gas washing absorber 7, induced draft fan and chimney 9;

wherein feeding device 1 comprises industrial grade vanadium pentoxide hopper 1-1, industrial grade vanadium pentoxide screw feeder 1-2, carbon powder hopper 1-3 and carbon powder screw feeder 1-4;

low temperature chlorination fluidized bed 2 comprises chlorination bed feeder 2-1, chlorination fluidized bed body 2-2, chlorination bed cyclone separator 2-3, flue gas heat exchanger 2-4, flue gas condenser 2-5, chlorination bed acid-seal tank 2-6 and chlorination bed spiral slag-discharging device 2-7;

rectification and purification device 3 comprises distilling still 3-1, rectifying column 3-2, distillate condenser 3-3, reflux liquid collecting tank 3-4, silicon-containing vanadium oxytrichloride storage tank 3-5, rectification section acid-seal tank 3-6, high-purity vanadium oxytrichloride condenser 3-7, and high-purity vanadium oxytrichloride storage tank 3-8;

gas phase ammonification fluidized bed 4 comprises ammonification bed air purifier 4-1, ammonification bed gas heater 4-2, vanadium oxytrichloride nozzle 4-3, gas phase ammonification fluidized bed body 4-4, ammonification bed cyclone separator 4-5, and ammonification bed discharger 4-6;

ammonium metavanadate feeding device 5 comprises ammonium metavanadate hopper 5-1 and ammonium metavanadate screw feeder 5-2;

calcination fluidized bed 6 comprises calcination bed air purifier 6-1, calcination bed gas heater 6-2, calcination bed feeder 6-3, calcination fluidized bed body 6-4, calcination bed cyclone separator 6-5 and high-purity vanadium pentoxide hopper 6-6;

wherein a feed outlet at the bottom of industrial grade vanadium pentoxide hopper 1-1 is connected with a feed inlet of industrial grade vanadium pentoxide screw feeder 1-2; a feed outlet at the bottom of carbon powder hopper 1-3 is connected with a feed inlet of carbon powder screw feeder 1-4; and a feed outlet of industrial grade vanadium pentoxide screw feeder 1-2 and a feed outlet of carbon powder screw feeder 1-4 are both connected with a feed inlet of chlorination bed feeder 2-1 through a pipeline;

a feed discharge opening of chlorination bed feeder 2-1 is connected with a feed inlet at the upper part of chlorination fluidized bed body 2-2 through a pipeline; a gas inlet at the bottom of chlorination bed feeder 2-1 is connected with a nitrogen gas source main pipe through a pipeline; chlorination bed cyclone separator 2-3 is provided at the center of the top of the expansion section of chlorination fluidized bed body 2-2; a gas outlet at the top of chlorination bed cyclone separator 2-3 is connected with a hot flue gas inlet of flue gas heat exchanger 2-4 through a pipeline; a cold flue gas outlet of flue gas heat exchanger 2-4 is connected with a gas inlet of flue gas condenser 2-5 through a pipeline; a gas outlet of flue gas condenser 2-5 is connected with a gas inlet of chlorination bed acid-seal tank 2-6 through a pipeline; a gas outlet of chlorination bed acid-seal tank 2-6 is connected with a gas inlet of tail gas washing absorber 7 through a pipeline; a slag-discharge opening at the lower part of chlorination fluidized bed body 2-2 is connected with a feed inlet of chlorination bed spiral slag-discharging device 2-7 through a pipeline; a gas inlet at the bottom of chlorination fluidized bed body 2-2 is connected with a hot gas outlet of flue gas heat exchanger 2-4 through a pipeline; and a cold gas inlet of flue gas heat exchanger 2-4 is connected with a chlorine gas source main pipe, the nitrogen gas source main pipe and a compressed air main pipe through pipelines, respectively;

a liquid outlet at the bottom of flue gas condenser 2-5 is connected with a feed inlet of rectifying column 3-2 through a pipeline; a steam outlet of distilling still 3-1 is connected with a steam inlet of rectifying column 3-2 through a pipeline; a backflow inlet of distilling still 3-1 is connected with a liquid reflux outlet at the bottom of rectifying column 3-2 through a pipeline; a gas outlet at the top of rectifying column 3-2 is connected with a gas inlet of distillate condenser 3-3 through a pipeline; a liquid outlet of distillate condenser 3-3 is connected with a liquid inlet of reflux liquid collecting tank 3-4 through a pipeline; a reflux liquid outlet of reflux liquid collecting tank 3-4 is connected with a reflux liquid inlet at the top of rectifying column 3-2 through a pipeline; a feed discharge opening of reflux liquid collecting tank 3-4 is connected with an inlet of silicon-containing vanadium oxytrichloride storage tank 3-5 through a pipeline; an exhaust gas outlet of silicon-containing vanadium oxytrichloride storage tank 3-5 is connected with a gas inlet of rectification section acid-seal tank 3-6 through a pipeline; a gas outlet of rectification section acid-seal tank 3-6 is connected with a gas inlet of tail gas washing absorber 7 through a pipeline; a rectificate outlet of rectifying column 3-2 is connected with a gas inlet of high-purity vanadium oxytrichloride condenser 3-7 through a pipeline; a liquid outlet of high-purity vanadium oxytrichloride condenser 3-7 is connected with a liquid inlet of high-purity vanadium oxytrichloride storage tank 3-8 through a pipeline; and an underflow outlet is provided at the bottom of distilling still 3-1;

a gas inlet of ammonification bed air purifier 4-1 is connected with the compressed air main pipe through a pipeline; a gas outlet of ammonification bed air purifier 4-1 is connected with a gas inlet of ammonification bed gas heater 4-2, a gas inlet of vanadium oxytrichloride nozzle 4-3, and a gas inlet at the bottom of ammonification bed discharger 4-6 through pipelines, respectively; the gas inlet of ammonification bed gas heater 4-2 is connected with an ultrapure water main pipe and a purified liquid ammonia main pipe through pipelines; a combustion-supporting wind inlet and a fuel inlet of a combustion nozzle of ammonification bed gas heater 4-2 are respectively connected with the compressed air main pipe and a fuel main pipe through pipelines; a gas outlet of ammonification bed gas heater 4-2 is connected with a gas inlet at the bottom of gas phase ammonification fluidized bed body 4-4 through a pipeline; a liquid outlet of high-purity vanadium oxytrichloride storage tank 3-8 is connected with a vanadium oxytrichloride inlet of vanadium oxytrichloride nozzle 4-3 through a pipeline; ammonification bed cyclone separator 4-5 is provided at the center of the top of the expansion section of gas phase ammonification fluidized bed body 4-4; a gas outlet at the top of ammonification bed cyclone separator 4-5 is connected with a tail gas treatment unit through a pipeline; a feed discharge opening at the upper part of gas phase ammonification fluidized bed body 4-4 is connected with a feed inlet of ammonification bed discharger 4-6 through a pipeline; and a feed discharge opening of ammonification bed discharger 4-6 is connected with a feed inlet of ammonium metavanadate hopper 5-1 through a pipeline;

a feed outlet at the bottom of ammonium metavanadate hopper 5-1 is connected with a feed inlet of ammonium metavanadate screw feeder 5-2; and a feed discharge opening of ammonium metavanadate screw feeder 5-2 is connected with a feed inlet of calcination bed feeder 6-3 through a pipeline;

a gas inlet of calcination bed air purifier 6-1 is connected with the compressed air main pipe through a pipeline; a gas outlet of calcination bed air purifier 6-1 is connected with a gas inlet of calcination bed gas heater 6-2 and a gas inlet at the bottom of calcination bed feeder 6-3 through pipelines, respectively; a combustion-supporting wind inlet and a fuel inlet of a combustion nozzle of calcination bed gas heater 6-2 are respectively connected with the compressed air main pipe and the fuel main pipe through pipelines; a gas outlet of calcination bed gas heater 6-2 is connected with a gas inlet at the bottom of calcination fluidized bed body 6-4 through a pipeline; a feed discharge opening of calcination bed feeder 6-3 is connected with a feed inlet at the lower part of calcination fluidized bed body 6-4 through a pipeline; a gas outlet at the top of calcination fluidized bed body 6-4 is connected with a gas inlet of calcination bed cyclone separator 6-5 through a pipeline; a powder outlet at the bottom of calcination bed cyclone separator 6-5 is connected with a feed inlet of an ammonium chloride hopper through a pipeline; a gas outlet at the top of calcination bed cyclone separator 6-5 is connected with the tail gas treatment unit through a pipeline; and a feed discharge opening at the upper part of calcination fluidized bed body 6-4 is connected with a feed inlet of high-purity vanadium pentoxide hopper 6-6 through a pipeline;

a gas outlet of tail gas washing absorber 7 is connected with a gas inlet of induced draft fan 8 through a pipeline; and a gas outlet of induced draft fan 8 is connected with a gas inlet at the bottom of chimney 9 through a pipeline.

The present invention further provides a method for purifying and preparing high-purity vanadium pentoxide powder based on the above system, comprising the following steps:

allowing industrial grade vanadium pentoxide powder in industrial grade vanadium pentoxide hopper 1-1 and carbon powder in carbon powder hopper 1-3 to enter chlorination bed feeder 2-1 simultaneously through industrial grade vanadium pentoxide screw feeder 1-2 and carbon powder screw feeder 1-4 respectively and be mixed therein, and then enter chlorination fluidized bed body 2-2; allowing chlorine gas from the chlorine gas source main pipe, nitrogen gas from the nitrogen gas source main pipe and air from the compressed air main pipe to be preheated by exchanging heat with chlorination flue gas by flue gas heat exchanger 2-4, and then enter chlorination fluidized bed body 2-2 to allow the vanadium pentoxide, the carbon powder and other powder materials to be kept at a fluidized state and chemically reacted, wherein the air enables a part of the carbon powder to combust to provide heat for maintaining the temperature of the fluid bed, and the chlorine gas and the carbon powder function together to make vanadium pentoxide and a small amount of impurities chlorinated, to form chlorinated residues and chlorination flue gas rich in vanadium oxytrichloride; discharging the chlorinated residues through the slag-discharge opening at the lower part of chlorination fluidized bed body 2-2 and chlorination bed spiral slag-discharging device 2-7; and allowing the chlorination flue gas to be subjected to dust removing by chlorination bed cyclone separator 2-3 and fall back to chlorination fluidized bed body 2-2, and then be precooled by flue gas heat exchanger 2-4 and enter flue gas condenser 2-5, such that vanadium oxytrichloride therein is condensed to form a crude vanadium oxytrichloride liquid and the remaining tail gas enters tail gas washing absorber 7 through chlorination bed acid-seal tank 2-6;

allowing the crude vanadium oxytrichloride liquid formed by flue gas condenser 2-5 to enter rectifying column 3-2 and distilling still 3-1 to be subjected to rectification operation, to obtain a vanadium-rich waste rich in high-boiling-point impurity, silicon-containing vanadium oxytrichloride vapor rich in low-boiling-point impurities and high-purity vanadium oxytrichloride vapor, wherein the vanadium-rich waste is used for the subsequent recovery of vanadium; condensing the silicon-containing vanadium oxytrichloride vapor into liquid by distillate condenser 3-3, wherein a part of the liquid returns to rectifying column 3-2 through reflux liquid collecting tank 3-4, and the remaining liquid enters silicon-containing vanadium oxytrichloride storage tank 3-5; transmitting the exhaust gas produced in silicon-containing vanadium oxytrichloride storage tank 3-5 to tail gas washing absorber 7 through rectification section acid-seal tank 3-6, wherein silicon-containing vanadium oxytrichloride can be applied in the field of chemical engineering such as the field of catalysis; and condensing the high-purity vanadium oxytrichloride vapor into liquid by high-purity vanadium oxytrichloride condenser 3-7 and allowing the liquid to enter high-purity vanadium oxytrichloride storage tank 3-8;

allowing the high-purity vanadium oxytrichloride from high-purity vanadium oxytrichloride storage tank 3-8 to be carried by purified air from ammonification bed air purifier 4-1 into gas phase ammonification fluidized bed body 4-4 via vanadium oxytrichloride nozzle 4-3; preheating ultrapure water, purified liquid ammonia and the purified air by ammonification bed gas heater 4-2 and then transmitting them to gas phase ammonification fluidized bed body 4-4, to keep the powder in the bed at a fluidized state and subject vanadium oxytrichloride to hydrolysis and ammonification to generate ammonium metavanadate powder containing ammonium chloride, wherein the ammonium metavanadate powder containing ammonium chloride enters ammonium metavanadate hopper 5-1 after discharged by ammonification bed discharger 4-6, and the produced ammonia-containing ammonified flue gas is subjected to dust removing by ammonification bed cyclone separator 4-5 and then transmitted to the tail gas treatment unit for treatment;

allowing the ammonium metavanadate powder containing ammonium chloride in ammonium metavanadate hopper 5-1 to enter calcination fluidized bed body 6-4 through ammonium metavanadate screw feeder 5-2 and calcination bed feeder 6-3 in turn; allowing compressed air to be purified by calcination bed air purifier 6-1 and preheated by calcination bed gas heater 6-2 in turn and then enter calcination fluidized bed body 6-4, to keep the powder in the bed at a fluidized state and subject the ammonium metavanadate material containing ammonium chloride to thermal decomposition to obtain a high-purity vanadium pentoxide powder product, and allowing the product to enter high-purity vanadium pentoxide hopper 6-6 through the feed discharge opening at the upper part of calcination fluidized bed body 6-4; allowing the calcination flue gas produced by the calcination decomposition to enter calcination bed cyclone separator 6-5 and be cooled down to separate out ammonium chloride, and transmitting the calcination flue gas to the tail gas treatment unit for treatment after dust removal; and transmitting the ammonium chloride powder collected by calcination bed cyclone separator 6-5 to the ammonium chloride hopper;

transmitting the gas discharged from tail gas washing absorber 7 after absorption treatment with an alkali solution to chimney 9 then to vent through induced draft fan 8.

The first characteristic of the present invention lies in that: in chlorination fluidized bed body 2-2, the amount of the carbon powder added in the chlorination process is 10%-20% of the mass of the industrial grade vanadium pentoxide powder; and in the chlorination, the operation temperature is 300-500° C. and the average residence time of the powder is 30-80 min.

The second characteristic of the present invention lies in that: in rectifying column 3-2, the number of trays in the rectification section is 5-10, and the number of trays in the stripping section is 10-20 in the rectification operation; and in the rectification operation, the reflux ratio (i.e., the ratio of the quantity of reflux at the top of the column to the amount of the discharged material) is kept at 15-40.

The third characteristic of the present invention lies in that: in gas phase ammonification fluidized bed body 4-4, ammonium metavanadate is prepared by gas phase ammonification of the high-purity vanadium oxytrichloride, and in the gas phase ammonification, the operation temperature is 130-250° C., the molar ratio of water vapor to ammonia gas is 0.5-0.8, and the molar ratio of ammonia gas to vanadium oxytrichloride is 3.5-4.5.

The fourth characteristic of the present invention lies in that: in calcination fluidized bed body 6-4, the thermal decomposition of the ammonium metavanadate containing ammonium chloride is achieved by fluidization calcination, and in the calcination, the operation temperature is 400-650° C., and the average residence time of the powder is 60-180 min.

The purity of the high-purity vanadium pentoxide powder prepared by the present invention is above 4N. Compared with the prior art, the present invention has the following outstanding advantages:

(1) Through heat exchange between the chlorinating gas and the chlorination flue gas, preheating of the chlorinating gas is achieved while the flue gas is cooled, which makes the temperature distribution in the chlorination reactor more uniform, thereby improving the efficiency of low temperature chlorination of vanadium raw material effectively.

(2) By adding an appropriate amount of air to enable a part of carbon powder to combust, a balanced heat supply and temperature regulation during the chlorination are implemented, thereby stabilizing the operation temperature in the chlorination, increasing the efficiency of the chlorination reaction, ensuring good selectivity in the chlorination, and avoiding side reactions such as generation of vanadium tetrachloride.

(3) By transmitting vanadium oxytrichloride which is purified by rectification to the gas phase ammonification fluidized bed via the nozzle to conduct hydrolysis and ammonification on the vanadium oxytrichloride, an ammonium metavanadate powder containing ammonium chloride is obtained. As compared to the traditional hydrolysis/ammonium salt precipitation, the production of ammonium chloride waste salty water can be avoided effectively.

(4) By conducting fluidization calcination on the ammonium metavanadate containing ammonium chloride, ammonium metavanadate is decomposed into the high-purity vanadium pentoxide product, and ammonium chloride is also decomposed and discharged with the flue gas, and an ammonium chloride product can be obtained after cooling, thereby realizing the preparation of a high-purity product and recovery of ammonium chloride effectively.

The present invention has the advantages of favorable adaptability to a raw material, good selectivity in low temperature chlorination, no discharge of contaminated wastewater, low energy consumption in production and low operation cost, stable product quality and so on, and is suitable for the large scale industrial production of the high-purity vanadium pentoxide powder with a purity of above 4N, with good economic efficiency and social benefits.

BRIEF DESCRIPTION OF THE DRAWINGS

The accompanying drawing is used to provide further illustration of the present invention and constitutes a part of the specification. It is used to explain the present invention together with the examples of the present invention, rather than limit the present invention.

FIG. 1 is a schematic diagram illustrating the configuration of a system for producing high-purity vanadium tetraoxide powder according to the present invention.

REFERENCE SIGNS

-   -   1 Feeding device     -   1-1 Industrial grade vanadium pentoxide hopper     -   1-2 Industrial grade vanadium pentoxide screw feeder     -   1-3 Carbon powder hopper     -   1-4 Carbon powder screw feeder     -   2 Low temperature chlorination fluidized bed     -   2-1 Chlorination bed feeder     -   2-2 Chlorination fluidized bed body     -   2-3 Chlorination bed cyclone separator     -   2-4 Flue gas heat exchanger     -   2-5 Flue gas condenser     -   2-6 Chlorination bed acid-seal tank     -   2-7 Chlorination bed spiral slag-discharging device     -   3 Rectification and purification device     -   3-1 Distilling still     -   3-2 Rectifying column     -   3-3 Distillate condenser     -   3-4 Reflux liquid collecting tank     -   3-5 Silicon-containing vanadium oxytrichloride storage tank     -   3-6 Rectification section acid-seal tank     -   3-7 High-purity vanadium oxytrichloride condenser     -   3-8 High-purity vanadium oxytrichloride storage tank     -   4 Gas phase ammonification fluidized bed     -   4-1 Ammonification bed air purifier     -   4-2 Ammonification bed gas heater     -   4-3 Vanadium oxytrichloride nozzle     -   4-4 Gas phase ammonification fluidized bed body     -   4-5 Ammonification bed cyclone separator     -   4-6 Ammonification bed discharger     -   5 Ammonium metavanadate feeding device     -   5-1 Ammonium metavanadate hopper     -   5-2 Ammonium metavanadate screw feeder     -   6 Calcination fluidized bed     -   6-1 Calcination bed air purifier     -   6-2 Calcination bed gas heater     -   6-3 Calcination bed feeder     -   6-4 Calcination fluidized bed body     -   6-5 Calcination bed cyclone separator     -   6-6 High-purity vanadium pentoxide hopper     -   7 Tail gas washing absorber     -   8 Induced draft fan     -   9 Chimney

DETAILED DESCRIPTION OF THE INVENTION

In order to make the object, technical solution and advantages of the present invention be clearer, the technical solution in the examples of the present invention will be described clearly and completely below with reference to the accompanying drawing of the examples of the present invention. Obviously, the described examples are only a part of the examples of the present invention, not all examples. It is worth noting that the examples are merely used for illustrating the technical solution of the present invention, rather than limiting the present invention. FIG. 1 is a schematic diagram illustrating a system for purifying and preparing high-purity vanadium pentoxide powder according to the present invention.

Referring to FIG. 1, the system for purifying and preparing high-purity vanadium pentoxide powder used in this example comprises feeding device 1, low temperature chlorination fluidized bed 2, rectification and purification device 3, gas phase ammonification fluidized bed 4, ammonium metavanadate feeding device 5, calcination fluidized bed 6, tail gas washing absorber 7, induced draft fan 8 and a chimney 9;

wherein feeding device 1 comprises industrial grade vanadium pentoxide hopper 1-1, industrial grade vanadium pentoxide screw feeder 1-2, carbon powder hopper 1-3 and carbon powder screw feeder 1-4;

low temperature chlorination fluidized bed 2 comprises chlorination bed feeder 2-1, chlorination fluidized bed body 2-2, chlorination bed cyclone separator 2-3, flue gas heat exchanger 2-4, flue gas condenser 2-5, chlorination bed acid-seal tank 2-6 and chlorination bed spiral slag-discharging device 2-7;

rectification and purification device 3 comprises distilling still 3-1, rectifying column 3-2, distillate condenser 3-3, reflux liquid collecting tank 3-4, silicon-containing vanadium oxytrichloride storage tank 3-5, rectification section acid-seal tank 3-6, high-purity vanadium oxytrichloride condenser 3-7, and high-purity vanadium oxytrichloride storage tank 3-8;

gas phase ammonification fluidized bed 4 comprises ammonification bed air purifier 4-1, ammonification bed gas heater 4-2, vanadium oxytrichloride nozzle 4-3, gas phase ammonification fluidized bed body 4-4, ammonification bed cyclone separator 4-5, and ammonification bed discharger 4-6;

ammonium metavanadate feeding device 5 comprises ammonium metavanadate hopper 5-1 and ammonium metavanadate screw feeder 5-2;

calcination fluidized bed 6 comprises calcination bed air purifier 6-1, calcination bed gas heater 6-2, calcination bed feeder 6-3, calcination fluidized bed body 6-4, calcination bed cyclone separator 6-5 and high-purity vanadium pentoxide hopper 6-6;

wherein a feed outlet at the bottom of industrial grade vanadium pentoxide hopper 1-1 is connected with a feed inlet of industrial grade vanadium pentoxide screw feeder 1-2; a feed outlet at the bottom of carbon powder hopper 1-3 is connected with a feed inlet of carbon powder screw feeder 1-4; and a feed outlet of industrial grade vanadium pentoxide screw feeder 1-2 and a feed outlet of carbon powder screw feeder 1-4 are both connected with a feed inlet of chlorination bed feeder 2-1 through a pipeline;

a feed discharge opening of chlorination bed feeder 2-1 is connected with a feed inlet at the upper part of chlorination fluidized bed body 2-2 through a pipeline; a gas inlet at the bottom of chlorination bed feeder 2-1 is connected with a nitrogen gas source main pipe through a pipeline; chlorination bed cyclone separator 2-3 is provided at the center of the top of the expansion section of chlorination fluidized bed body 2-2; a gas outlet at the top of chlorination bed cyclone separator 2-3 is connected with a hot flue gas inlet of flue gas heat exchanger 2-4 through a pipeline; a cold flue gas outlet of flue gas heat exchanger 2-4 is connected with a gas inlet of flue gas condenser 2-5 through a pipeline; a gas outlet of flue gas condenser 2-5 is connected with a gas inlet of chlorination bed acid-seal tank 2-6 through a pipeline; a gas outlet of chlorination bed acid-seal tank 2-6 is connected with a gas inlet of tail gas washing absorber 7 through a pipeline; a slag-discharge opening at the lower part of chlorination fluidized bed body 2-2 is connected with a feed inlet of chlorination bed spiral slag-discharging device 2-7 through a pipeline; a gas inlet at the bottom of chlorination fluidized bed body 2-2 is connected with a hot gas outlet of flue gas heat exchanger 2-4 through a pipeline; and a cold gas inlet of flue gas heat exchanger 2-4 is connected with a chlorine gas source main pipe, the nitrogen gas source main pipe and a compressed air main pipe through a pipeline, respectively;

a liquid outlet at the bottom of flue gas condenser 2-5 is connected with a feed inlet of rectifying column 3-2 through a pipeline; a steam outlet of distilling still 3-1 is connected with a steam inlet of rectifying column 3-2 through a pipeline; a backflow inlet of distilling still 3-1 is connected with a liquid reflux outlet at the bottom of rectifying column 3-2 through a pipeline; a gas outlet at the top of rectifying column 3-2 is connected with a gas inlet of distillate condenser 3-3 through a pipeline; a liquid outlet of distillate condenser 3-3 is connected with a liquid inlet of reflux liquid collecting tank 3-4 through a pipeline; a reflux liquid outlet of reflux liquid collecting tank 3-4 is connected with a reflux liquid inlet at the top of rectifying column 3-2 through a pipeline; a feed discharge opening of reflux liquid collecting tank 3-4 is connected with an inlet of silicon-containing vanadium oxytrichloride storage tank 3-5 through a pipeline; an exhaust gas outlet of silicon-containing vanadium oxytrichloride storage tank 3-5 is connected with a gas inlet of rectification section acid-seal tank 3-6 through a pipeline; a gas outlet of rectification section acid-seal tank 3-6 is connected with a gas inlet of tail gas washing absorber 7 through a pipeline; a rectificate outlet of rectifying column 3-2 is connected with a gas inlet of high-purity vanadium oxytrichloride condenser 3-7 through a pipeline; a liquid outlet of high-purity vanadium oxytrichloride condenser 3-7 is connected with a liquid inlet of high-purity vanadium oxytrichloride storage tank 3-8 through a pipeline; and an underflow outlet is provided at the bottom of distilling still 3-1;

a gas inlet of ammonification bed air purifier 4-1 is connected with the compressed air main pipe through a pipeline; a gas outlet of ammonification bed air purifier 4-1 is connected with a gas inlet of ammonification bed gas heater 4-2, a gas inlet of vanadium oxytrichloride nozzle 4-3, and a gas inlet at the bottom of ammonification bed discharger 4-6 through a pipeline, respectively; the gas inlet of ammonification bed gas heater 4-2 is connected with a ultrapure water main pipe and a purified liquid ammonia main pipe through a pipeline; a combustion-supporting wind inlet and a fuel inlet of a combustion nozzle of ammonification bed gas heater 4-2 are respectively connected with the compressed air main pipe and a fuel main pipe through a pipeline; a gas outlet of ammonification bed gas heater 4-2 is connected with a gas inlet at the bottom of gas phase ammonification fluidized bed body 4-4 through a pipeline; a liquid outlet of high-purity vanadium oxytrichloride storage tank 3-8 is connected with a vanadium oxytrichloride inlet of vanadium oxytrichloride nozzle 4-3 through a pipeline; ammonification bed cyclone separator 4-5 is provided at the center of the top of the expansion section of gas phase ammonification fluidized bed body 4-4; a gas outlet at the top of ammonification bed cyclone separator 4-5 is connected with a tail gas treatment unit through a pipeline; a feed discharge opening at the upper part of gas phase ammonification fluidized bed body 4-4 is connected with a feed inlet of ammonification bed discharger 4-6 through a pipeline; and a feed discharge opening of ammonification bed discharger 4-6 is connected with a feed inlet of ammonium metavanadate hopper 5-1 through a pipeline;

a feed outlet at the bottom of ammonium metavanadate hopper 5-1 is connected with a feed inlet of ammonium metavanadate screw feeder 5-2; and a feed discharge opening of ammonium metavanadate screw feeder 5-2 is connected with a feed inlet of calcination bed feeder 6-3 through a pipeline;

a gas inlet of calcination bed air purifier 6-1 is connected with the compressed air main pipe through a pipeline; a gas outlet of calcination bed air purifier 6-1 is connected with a gas inlet of calcination bed gas heater 6-2 and a gas inlet at the bottom of calcination bed feeder 6-3 through a pipeline, respectively; a combustion-supporting wind inlet and a fuel inlet of a combustion nozzle of calcination bed gas heater 6-2 are respectively connected with the compressed air main pipe and the fuel main pipe through a pipeline; a gas outlet of calcination bed gas heater 6-2 is connected with a gas inlet at the bottom of calcination fluidized bed body 6-4 through a pipeline; a feed discharge opening of calcination bed feeder 6-3 is connected with a feed inlet at the lower part of calcination fluidized bed body 6-4 through a pipeline; a gas outlet at the top of calcination fluidized bed body 6-4 is connected with a gas inlet of calcination bed cyclone separator 6-5 through a pipeline; a powder outlet at the bottom of calcination bed cyclone separator 6-5 is connected with a feed inlet of an ammonium chloride hopper through a pipeline; a gas outlet at the top of calcination bed cyclone separator 6-5 is connected with the tail gas treatment unit through a pipeline; and a feed discharge opening at the upper part of calcination fluidized bed body 6-4 is connected with a feed inlet of high-purity vanadium pentoxide hopper 6-6 through a pipeline;

a gas outlet of tail gas washing absorber 7 is connected with a gas inlet of induced draft fan 8 through a pipeline; and a gas outlet of induced draft fan 8 is connected with a gas inlet at the bottom of chimney 9 through a pipeline.

The above system is used in this example to purify and prepare high-purity vanadium pentoxide powder. The specific method comprises the following steps. Industrial grade vanadium pentoxide powder in industrial grade vanadium pentoxide hopper 1-1 and carbon powder in carbon powder hopper 1-3 enter chlorination bed feeder 2-1 simultaneously through industrial grade vanadium pentoxide screw feeder 1-2 and carbon powder screw feeder 1-4 respectively and are mixed therein, and then enter chlorination fluidized bed body 2-2; chlorine gas from the chlorine gas source main pipe, nitrogen gas from the nitrogen gas source main pipe and air from the compressed air main pipe are preheated by exchanging heat with chlorination flue gas by flue gas heat exchanger 2-4, and then enter chlorination fluidized bed body 2-2 to allow the vanadium pentoxide, the carbon powder and other powder materials at a fluidized state and chemically reacted, wherein the air enables a part of the carbon powder to combust to provide heat for maintaining the temperature of the fluid bed, and the chlorine gas and the carbon powder function together to make vanadium pentoxide and a small amount of impurities [[be]] chlorinated, to form chlorinated residues and chlorination flue gas rich in vanadium oxytrichloride; the chlorinated residues are discharged through the slag-discharge opening at the lower part of chlorination fluidized bed body 2-2 and chlorination bed spiral slag-discharging device 2-7; and the chlorination flue gas is subjected to dust removing by chlorination bed cyclone separator 2-3 and falls back to chlorination fluidized bed body 2-2, and then is precooled by flue gas heat exchanger 2-4 and enters flue gas condenser 2-5, such that vanadium oxytrichloride therein is condensed to form a crude vanadium oxytrichloride liquid and the remaining tail gas enters tail gas washing absorber 7 through chlorination bed acid-seal tank 2-6;

the crude vanadium oxytrichloride liquid formed by flue gas condenser 2-5 enters rectifying column 3-2 and distilling still 3-1 to be subjected to rectification operation, to obtain a vanadium-rich waste rich in high-boiling-point impurities, silicon-containing vanadium oxytrichloride vapor rich in low-boiling-point impurities and high-purity vanadium oxytrichloride vapor, wherein the vanadium-rich waste is used for the subsequent recovery of vanadium; the silicon-containing vanadium oxytrichloride vapor is condensed into liquid by distillate condenser 3-3, wherein a part of the liquid returns to rectifying column 3-2 through reflux liquid collecting tank 3-4, and the remaining liquid enters silicon-containing vanadium oxytrichloride storage tank 3-5; the exhaust gas produced in silicon-containing vanadium oxytrichloride storage tank 3-5 is transmitted to tail gas washing absorber 7 through rectification section acid-seal tank 3-6, wherein the silicon-containing vanadium oxytrichloride can be applied in the field of chemical engineering such as the field of catalysis; and the high-purity vanadium oxytrichloride vapor is condensed into liquid by high-purity vanadium oxytrichloride condenser 3-7 and then enters the high-purity vanadium oxytrichloride storage tank 3-8;

the high-purity vanadium oxytrichloride from high-purity vanadium oxytrichloride storage tank 3-8 is carried by purified air from ammonification bed air purifier 4-1 into gas phase ammonification fluidized bed body 4-4 via vanadium oxytrichloride nozzle 4-3; ultrapure water, purified liquid ammonia and the purified air are preheated by ammonification bed gas heater 4-2 and then transmitted to gas phase ammonification fluidized bed body 4-4, to keep the powder in the bed at a fluidized state and subject vanadium oxytrichloride to hydrolysis and ammonification to generate ammonium metavanadate powder containing ammonium chloride, wherein the ammonium metavanadate powder containing ammonium chloride enters ammonium metavanadate hopper 5-1 after discharged by ammonification bed discharger 4-6, and the produced ammonia-containing ammonified flue gas is subjected to dust removing by ammonification bed cyclone separator 4-5 and then transmitted to the tail gas treatment unit for treatment;

the ammonium metavanadate powder containing ammonium chloride in ammonium metavanadate hopper 5-1 enters calcination fluidized bed body 6-4 through ammonium metavanadate screw feeder 5-2 and calcination bed feeder 6-3 in turn; compressed air is purified by calcination bed air purifier 6-1 and preheated by calcination bed gas heater 6-2 in turn and then enters calcination fluidized bed body 6-4, to keep the powder in the bed at a fluidized state and subject the ammonium metavanadate material containing ammonium chloride to thermal decomposition to obtain a high-purity vanadium pentoxide powder product, and the product enters high-purity vanadium pentoxide hopper 6-6 through the feed discharge opening at the upper part of calcination fluidized bed body 6-4; the calcination flue gas produced from the calcination decomposition enters calcination bed cyclone separator 6-5 and be cooled down therein, such that ammonium chloride is separated out, and the calcination flue gas is transmitted to the tail gas treatment unit for treatment after dust removal; and the ammonium chloride powder collected by calcination bed cyclone separator 6-5 is transmitted to the ammonium chloride hopper;

the gas discharged from tail gas washing absorber 7 after absorption treatment with an alkali solution is transmitted to chimney 9 then to vent through induced draft fan 8.

In this example, the industrial grade vanadium pentoxide powder was used as the raw material and its chemical composition is shown in Table 1. The throughput is 70 kg/h, and the high-purity vanadium pentoxide product was prepared by low temperature chlorination, rectification of vanadium oxytrichloride, gas phase ammonification and calcination.

TABLE 1 Chemical composition of the industrial grade vanadium pentoxide raw material used in the example (wt %) V₂O₅ Si Ca Al Ti Fe Mn Na K S 98.8 0.0150 0.0275 0.0099 0.0260 0.0971 0.0293 0.1385 0.0714 0.1274

The operation conditions are as follows: in chlorination fluidized bed body 2-2, the amount of the carbon powder added in the low temperature chlorination process is 10% of the mass of the industrial grade vanadium pentoxide powder, and in the chlorination, the operation temperature is 500° C. and the average residence time of the powder is 30 min; in rectifying column 3-2, the number of trays in the rectification section is 5, and the number of trays in the stripping section is 10 in the rectification operation, and the reflux ratio of the rectification operation is 40; in gas phase ammonification fluidized bed body 4-4, the operation temperature is 130° C., the molar ratio of water vapor to ammonia gas is 0.5, and the molar ratio of ammonia gas to vanadium oxytrichloride is 4.5 in the gas phase ammonification; in calcination fluidized bed body 6-4, the operation temperature is 400° C. and the average residence time of the powder is 180 min in the calcination. Under such operation conditions, the direct recovery rate of vanadium reached 80%, and the purity of the high-purity vanadium pentoxide product reached 99.995 wt % (4N5).

The operation conditions are as follows: in chlorination fluidized bed body 2-2, the amount of the carbon powder added in the low temperature chlorination process is 20% of the mass of the industrial grade vanadium pentoxide powder, and in the chlorination, the operation temperature is 300° C. and the average residence time of the powder is 80 min; in rectifying column 3-2, the number of trays in the rectification section is 10, and the number of trays in the stripping section is 20 in the rectification operation, and the reflux ratio of the rectification operation is 15; in gas phase ammonification fluidized bed body 4-4, the operation temperature is 250° C., the molar ratio of water vapor to ammonia gas is 0.8, and the molar ratio of ammonia gas to vanadium oxytrichloride is 3.5 in the gas phase ammonification; in calcination fluidized bed body 6-4, the operation temperature is 650° C. and the average residence time of the powder is 60 min in the calcination. Under such operation conditions, the direct recovery rate of vanadium reached 81%, and the purity of the high-purity vanadium pentoxide product reached 99.999 wt % (5N).

The details which are not illustrated in detail in the present invention belong to the well-known technologies in the art.

Of course, the present invention can also provide a variety of examples. According to the disclosure of the present invention, those skilled in the art can make various corresponding changes and transformations without departing from the spirit and essence of the present invention; however, these corresponding changes and transformations shall all fall within the protection scope of the claims of the present invention. 

What is claimed is:
 1. A system for purifying and preparing high-purity vanadium pentoxide powder, comprising a feeding device, a low temperature chlorination fluidized bed, a rectification and purification device, a gas phase ammonification fluidized bed, an ammonium metavanadate feeding device, a calcination fluidized bed, a tail gas washing absorber, an induced draft fan and a chimney; wherein the feeding device comprises an industrial grade vanadium pentoxide hopper, an industrial grade vanadium pentoxide screw feeder, a carbon powder hopper and a carbon powder screw feeder; the low temperature chlorination fluidized bed comprises a chlorination bed feeder, a chlorination fluidized bed body, a chlorination bed cyclone separator, a flue gas heat exchanger, a flue gas condenser, a chlorination bed acid-seal tank and a chlorination bed spiral slag-discharging device; the rectification and purification device comprises a distilling still, a rectifying column, a distillate condenser, a reflux liquid collecting tank, a silicon-containing vanadium oxytrichloride storage tank, a rectification section acid-seal tank, a high-purity vanadium oxytrichloride condenser, and a high-purity vanadium oxytrichloride storage tank; the gas phase ammonification fluidized bed comprises an ammonification bed air purifier, an ammonification bed gas heater, a vanadium oxytrichloride nozzle, a gas phase ammonification fluidized bed body, an ammonification bed cyclone separator, and an ammonification bed discharger; the ammonium metavanadate feeding device comprises an ammonium metavanadate hopper and an ammonium metavanadate screw feeder; the calcination fluidized bed comprises a calcination bed air purifier, a calcination bed gas heater, a calcination bed feeder, a calcination fluidized bed body, a calcination bed cyclone separator and a high-purity vanadium pentoxide hopper; wherein a feed outlet at the bottom of the industrial grade vanadium pentoxide hopper is connected with a feed inlet of the industrial grade vanadium pentoxide screw feeder; a feed outlet at the bottom of the carbon powder hopper is connected with a feed inlet of the carbon powder screw feeder; and a feed outlet of the industrial grade vanadium pentoxide screw feeder and a feed outlet of the carbon powder screw feeder are both connected with a feed inlet of the chlorination bed feeder through a pipeline; a feed discharge opening of the chlorination bed feeder is connected with a feed inlet at the upper part of the chlorination fluidized bed body through a pipeline; a gas inlet at the bottom of the chlorination bed feeder is connected with a nitrogen gas source main pipe through a pipeline; the chlorination bed cyclone separator is provided at the center of the top of the expansion section of the chlorination fluidized bed body; a gas outlet at the top of the chlorination bed cyclone separator is connected with a hot flue gas inlet of the flue gas heat exchanger through a pipeline; a cold flue gas outlet of the flue gas heat exchanger is connected with a gas inlet of the flue gas condenser through a pipeline; a gas outlet of the flue gas condenser is connected with a gas inlet of the chlorination bed acid-seal tank through a pipeline; a gas outlet of the chlorination bed acid-seal tank is connected with a gas inlet of the tail gas washing absorber through a pipeline; a slag-discharge opening at the lower part of the chlorination fluidized bed body is connected with a feed inlet of the chlorination bed spiral slag-discharging device through a pipeline; a gas inlet at the bottom of the chlorination fluidized bed body is connected with a hot gas outlet of the flue gas heat exchanger through a pipeline; and a cold gas inlet of the flue gas heat exchanger is connected with a chlorine gas source main pipe, the nitrogen gas source main pipe and a compressed air main pipe through pipelines, respectively; a liquid outlet at the bottom of the flue gas condenser is connected with a feed inlet of the rectifying column through a pipeline; a steam outlet of the distilling still is connected with a steam inlet of the rectifying column through a pipeline; a backflow inlet of the distilling still is connected with a liquid reflux outlet at the bottom of the rectifying column through a pipeline; a gas outlet at the top of the rectifying column is connected with a gas inlet of the distillate condenser through a pipeline; a liquid outlet of the distillate condenser is connected with a liquid inlet of the reflux liquid collecting tank through a pipeline; a reflux liquid outlet of the reflux liquid collecting tank is connected with a reflux liquid inlet at the top of the rectifying column through a pipeline; a feed discharge opening of the reflux liquid collecting tank is connected with an inlet of the silicon-containing vanadium oxytrichloride storage tank through a pipeline; an exhaust gas outlet of the silicon-containing vanadium oxytrichloride storage tank is connected with a gas inlet of the rectification section acid-seal tank through a pipeline; a gas outlet of the rectification section acid-seal tank is connected with a gas inlet of the tail gas washing absorber through a pipeline; a rectificate outlet of the rectifying column is connected with a gas inlet of the high-purity vanadium oxytrichloride condenser through a pipeline; a liquid outlet of the high-purity vanadium oxytrichloride condenser is connected with a liquid inlet of the high-purity vanadium oxytrichloride storage tank through a pipeline; and an underflow outlet is provided at the bottom of the distilling still; a gas inlet of the ammonification bed air purifier is connected with the compressed air main pipe through a pipeline; a gas outlet of the ammonification bed air purifier is connected with a gas inlet of the ammonification bed gas heater, a gas inlet of the vanadium oxytrichloride nozzle, and a gas inlet at the bottom of the ammonification bed discharger through pipelines, respectively; the gas inlet of the ammonification bed gas heater is connected with an ultrapure water main pipe and a purified liquid ammonia main pipe through pipelines; a combustion-supporting wind inlet and a fuel inlet of a combustion nozzle of the ammonification bed gas heater are respectively connected with the compressed air main pipe and a fuel main pipe through pipelines; a gas outlet of the ammonification bed gas heater is connected with a gas inlet at the bottom of the gas phase ammonification fluidized bed body through a pipeline; a liquid outlet of the high-purity vanadium oxytrichloride storage tank is connected with a vanadium oxytrichloride inlet of the vanadium oxytrichloride nozzle through a pipeline; the ammonification bed cyclone separator is provided at the center of the top of the expansion section of the gas phase ammonification fluidized bed body; a gas outlet at the top of the ammonification bed cyclone separator is connected with a tail gas treatment unit through a pipeline; a feed discharge opening at the upper part of the gas phase ammonification fluidized bed body is connected with a feed inlet of the ammonification bed discharger through a pipeline; and a feed discharge opening of the ammonification bed discharger is connected with a feed inlet of the ammonium metavanadate hopper through a pipeline; a feed outlet at the bottom of the ammonium metavanadate hopper is connected with a feed inlet of the ammonium metavanadate screw feeder; and a feed discharge opening of the ammonium metavanadate screw feeder is connected with a feed inlet of the calcination bed feeder through a pipeline; a gas inlet of the calcination bed air purifier is connected with the compressed air main pipe through a pipeline; a gas outlet of the calcination bed air purifier is connected with a gas inlet of the calcination bed gas heater and a gas inlet at the bottom of the calcination bed feeder through pipelines, respectively; a combustion-supporting wind inlet and a fuel inlet of a combustion nozzle of the calcination bed gas heater are respectively connected with the compressed air main pipe and the fuel main pipe through pipelines; a gas outlet of the calcination bed gas heater is connected with a gas inlet at the bottom of the calcination fluidized bed body through a pipeline; a feed discharge opening of the calcination bed feeder is connected with a feed inlet at the lower part of the calcination fluidized bed body through a pipeline; a gas outlet at the top of the calcination fluidized bed body is connected with a gas inlet of the calcination bed cyclone separator through a pipeline; a powder outlet at the bottom of the calcination bed cyclone separator is connected with a feed inlet of an ammonium chloride hopper through a pipeline; a gas outlet at the top of the calcination bed cyclone separator is connected with the tail gas treatment unit through a pipeline; and a feed discharge opening at the upper part of the calcination fluidized bed body is connected with a feed inlet of the high-purity vanadium pentoxide hopper through a pipeline; a gas outlet of the tail gas washing absorber is connected with a gas inlet of the induced draft fan through a pipeline; and a gas outlet of the induced draft fan is connected with a gas inlet at the bottom of the chimney through a pipeline.
 2. A method for purifying and preparing high-purity vanadium pentoxide powder using the system of claim 1, comprising the following steps: introducing industrial grade vanadium pentoxide powder in the industrial grade vanadium pentoxide hopper and carbon powder in the carbon powder hopper to the chlorination bed feeder simultaneously through the industrial grade vanadium pentoxide screw feeder and the carbon powder screw feeder respectively and be mixed therein, and then entering the chlorination fluidized bed body; preheating chlorine gas from the chlorine gas source main pipe, nitrogen gas from the nitrogen gas source main pipe and air from the compressed air main by exchanging heat with chlorination flue gas by the flue gas heat exchanger, and then entering the chlorination fluidized bed body to keep the vanadium pentoxide and the carbon powder at a fluidized state and chemically reacted, wherein the air enables a part of the carbon powder to combust to provide heat for maintaining the temperature of the low temperature chlorination fluidized bed, wherein the chlorine gas and the carbon powder function together to chlorinate vanadium pentoxide and a small amount of impurities, to form chlorinated residues and chlorination flue gas rich in vanadium oxytrichloride; discharging the chlorinated residues through the slag-discharge opening at the lower part of the chlorination fluidized bed body and the chlorination bed spiral slag-discharging device in turn; and removing dust from the chlorination flue gas by the chlorination bed cyclone separator, and then precooling the flue gas by the flue gas heat exchanger and passing through the flue gas condenser, such that vanadium oxytrichloride therein is condensed to form a crude vanadium oxytrichloride liquid and the remaining tail gas enters the tail gas washing absorber through the chlorination bed acid-seal tank; introducing the crude vanadium oxytrichloride liquid formed by the flue gas condenser to the rectifying column and the distilling still to be subjected to rectification operation, to obtain a vanadium-rich waste rich in high-boiling-point impurities, silicon-containing vanadium oxytrichloride vapor rich in low-boiling-point impurities and high-purity vanadium oxytrichloride vapor; condensing the silicon-containing vanadium oxytrichloride vapor into liquid by the distillate condenser, wherein a part of the liquid returns to the rectifying column through the reflux liquid collecting tank, and the remaining liquid enters the silicon-containing vanadium oxytrichloride storage tank; transmitting the exhaust gas produced in the silicon-containing vanadium oxytrichloride storage tank to the tail gas washing absorber through the rectification section acid-seal tank; and condensing the high-purity vanadium oxytrichloride vapor into liquid by the high-purity vanadium oxytrichloride condenser and introducing the liquid to the high-purity vanadium oxytrichloride storage tank; the high-purity vanadium oxytrichloride from the high-purity vanadium oxytrichloride storage tank is carried by purified air from the ammonification bed air purifier into the gas phase ammonification fluidized bed body via the vanadium oxytrichloride nozzle; preheating ultrapure water, purified liquid ammonia and the purified air by the ammonification bed gas heater and then transmitting them to the gas phase ammonification fluidized bed body, to keep the powder in the bed at a fluidized state and subject vanadium oxytrichloride to hydrolysis and ammonification to generate ammonium metavanadate powder containing ammonium chloride, wherein the ammonium metavanadate powder containing ammonium chloride enters the ammonium metavanadate hopper after discharged by the ammonification bed discharger, and the produced ammonia-containing ammonified flue gas is subjected to dust removing by the ammonification bed cyclone separator and then transmitted to the tail gas treatment unit for treatment; introducing the ammonium metavanadate powder containing ammonium chloride in the ammonium metavanadate hopper to the calcination fluidized bed body through the ammonium metavanadate screw feeder and the calcination bed feeder in turn; purifying compressed air by the calcination bed air purifier and preheating by the calcination bed gas heater in turn and then entering the calcination fluidized bed body, to keep the powder in the bed at a fluidized state and subject the ammonium metavanadate material containing ammonium chloride to thermal decomposition to obtain a high-purity vanadium pentoxide powder product, and introducing the product to the high-purity vanadium pentoxide hopper through the feed discharge opening at the upper part of the calcination fluidized bed body; introducing the calcination flue gas produced by the calcination decomposition to the calcination bed cyclone separator and be cooled down to separate out ammonium chloride, and transmitting the calcination flue gas to the tail gas treatment unit for treatment after dust removal; and transmitting the ammonium chloride powder collected by the calcination bed cyclone separator to the ammonium chloride hopper; transmitting the gas discharged from the tail gas washing absorber after absorption treatment with an alkali solution to the chimney then to vent through the induced draft fan.
 3. The method for purifying and preparing high-purity vanadium pentoxide powder according to claim 2, wherein in the chlorination fluidized bed body, the amount of the carbon powder added in the chlorination process is 10%-20% of the mass of the industrial grade vanadium pentoxide powder.
 4. The method for purifying and preparing high-purity vanadium pentoxide powder according to claim 2, wherein in the chlorination fluidized bed body, the operation temperature is 300-500° C. and the average residence time of the powder is 30-80 min in the chlorination.
 5. The method for purifying and preparing high-purity vanadium pentoxide powder according to claim 2, wherein in the rectifying column, the number of trays in the rectification section is 5-10, and the number of trays in the stripping section is 10-20 in the rectification operation.
 6. The method for purifying and preparing high-purity vanadium pentoxide powder according to claim 2, wherein the reflux ratio of the rectification operation is 15-40.
 7. The method for purifying and preparing high-purity vanadium pentoxide powder according to claim 2, wherein in the gas phase ammonification fluidized bed body, ammonium metavanadate is prepared by gas phase ammonification of the high-purity vanadium oxytrichloride, and in the gas phase ammonification, the operation temperature is 130-250° C., the molar ratio of water vapor to ammonia gas is 0.5-0.8, and the molar ratio of ammonia gas to vanadium oxytrichloride is 3.5-4.5.
 8. The method for purifying and preparing high-purity vanadium pentoxide powder according to claim 2, wherein in the calcination fluidized bed body, the thermal decomposition of the ammonium metavanadate containing ammonium chloride is achieved by fluidization calcination, and in the calcination, the operation temperature is 400-650° C., and the average residence time of the powder is 60-180 min. 